Polyoxymethylene pom resin
Acetal Copolymer
Descriptions:
1) High flow, high wear resistance and high strength
2)Antibacterial, acid resistance, alkali resistance, high hardness, good chemical stability
Application:
Electrical and electronic equipment, accessories, thin wall parts, car accessories, gear, valve parts, car inner decoration, pipeline, roller, bearing, pump parts.
| Property Item | Test Condition | Test Data | Test Method |
| Density | 1.14g/cm3 | ISO 1183 | |
| MFR | (190°C/2.16kg) | 9 g/10min | ISO 1133 |
| Tensile strength(yield) | 62Mpa | ISO 527 | |
| Tensile modulus | 2700Mpa | ISO 527 | |
| Flexural strength | 61Mpa | ISO 178 | |
| Flexural modulus | 2400Mpa | ISO 178 | |
| Elongation(yield) | 13% | ISO 527 | |
| Elongation at break | 30% | ISO 527 | |
| Notched IZOD impact strength | 7.5Kj/m² | ISO 180/1eA | |
| Charpy Notched Impact Strength | 7.5Kj/m² | ISO 179/1EA | |
| Ball-indentation hardness | (H 358/30) | 140Mpa | ISO 2039 |
| Rockwell hardness | (23°C) | 114R | ISO 2039 |
| Distortion temperature | (1.8Mpa) | 115°C | ISO 75 |
| Vicat softening point | (50N) | 150°C | ISO 306/B50 |
| Vicat softening point | (10N) | 163°C | ISO 306/A50 |
| Melting point | 172°C | ISO 3146 |